D517 Hardfacing Welding Electrode
Contact Info
- Add:河北省邢臺市信都區(qū)永康街533號, Zip:
- Contact: 韓吉英
- Tel:13833921539
- Email:2891465062@qq.com
Other Products
D517 Hardfacing Welding Electrode
GB/T 984 EDCr-B-15
Suitable for hardfacing of carbon steel or low-alloy steel shafts, valve components for superheated steam, mixer paddles, screw conveyor blades, etc.
A 2Cr13 type valve hardfacing electrode with a low-hydrogen sodium coating. The deposited metal is 2Cr13 martensitic high-chromium steel. The hardfacing layer has air-hardening properties and generally does not require heat treatment. It has uniform hardness, can be annealed and softened at 750–800°C, and can be rehardened by air cooling or oil quenching when heated to 950–1000°C.
Direct current reverse polarity (DC+)
Chemical Composition of Deposited Metal (%)
| Test Item | C | Cr | Total Other Elements |
| GB/T Standard | ≤0.25 | 10.00–16.00 | ≤5.00 |
| Example Value | 0.20 | 13.40 | —— |
Hardness of Hardfacing Metal (Air-cooled after welding, resistant to softening up to 500°C)
| Test Item | HRC (4 layers or more) |
| GB/T Standard | ≥45 |
Reference Current
| Electrode Diameter (mm) | Φ3.2 | Φ4.0 | Φ5.0 |
| Welding Current (A) | 80–120 | 120–160 | 160–200 |
1. Drying requirement: Electrodes must be baked at 300°C for 1 hour before use and used while still warm.
2. Preheat hardfacing components to above 300°C. Different heat treatments after welding can achieve corresponding hardness levels.
| Industry Category | Hardware & Tools/Welding Materials & Accessories/Other Welding Materials |
|---|---|
| Product Category | |
| Brand: | 金帝牌 |
| Spec: | 2.5/3.2/4.0/5.0mm |
| Stock: | 5000 |
| Manufacturer: | |
| Origin: | China / Hebei / Xingtaishi |