TPV 3160-Sarlink Series Elastomer
Price:TPV 3160
Other Products
Description
Additional Information
TPV 3160-Sarlink Series Elastomer is a globally branded thermoplastic vulcanizate, an innovative material with rubber-like properties that can be processed like plastic.TPV 3160-Sarlink Series Elastomer provides time-tested TPV expertise, a wide product range, excellent customer service, and fully colorable high-performance solutions for many complex application challenges.
TPV 3160-Sarlink Series Elastomer Features: Excellent performance in molding, appearance, and resistance to flexural fatigue.
| TPV 3160-Sarlink Series Elastomer Molding Method | Injection MoldingExtrusion | |||
TPV 3160-Sarlink Series Elastomer Technical Parameters
| Physical Properties | Value/Unit | Test Standard | Test Conditions |
|---|---|---|---|
Density | 0.94 g/cm3 | ASTM D792 | |
Shrinkage | |||
Longitudinal (Flow) | 1.6 % | Internal | 3mm thickness |
Transverse (Across Flow) | 1.3 % | Internal | 3mm thickness |
| Mechanical Properties | Value/Unit | Test Standard | Test Conditions |
Tensile Strength | |||
At 100% Elongation | 7.1 MPa | ASTM D 412 | Cross direction |
At 100% Elongation | 7.9 MPa | ASTM D 412 | Flow direction |
- | 13.5 MPa | ASTM D 412 | Cross direction |
- | 11.5 MPa | ASTM D 412 | Flow direction |
Elongation at Break | |||
Break (brk) | 746 % | ASTM D 412 | Cross direction |
Break (brk) | 570 % | ASTM D 412 | Flow direction |
Tear Strength | 64 kN/m | ASTM D 624 | Unnicked, Cross direction |
Compression Set | 62 % | ASTM D 395 | 125℃, 70Hrs |
Compression Set | 37 % | ASTM D 395 | 23℃, 22Hrs |
Compression Set | 53 % | ASTM D 395 | 70℃, 22Hrs |
| Impact Properties | Value/Unit | Test Standard | Test Conditions |
Brittleness Temperature | -59 °C | ISO 812 | |
| Hardness Properties | Value/Unit | Test Standard | Test Conditions |
Shore Hardness A | 90 A | ASTM D 2240 | 5sec, Extruded sample |
Shore Hardness A | 93 A | ASTM D 2240 | 5sec, Injection molded sample |
| Flammability Properties | Value/Unit | Test Standard | Test Conditions |
UL Flame Rating | |||
HB | - mm | UL94 | |
| Aging Properties | Value/Unit | Test Standard | Test Conditions |
Hardness (Thermal Aging) | 0 - | ASTM D573 | Change, 135℃, 1000Hrs |
Hardness (Thermal Aging) | 2 - | ASTM D573 | Change, 150℃, 168Hrs |
Tensile Strength (Thermal Aging) | 95 % | ASTM D573 | Retention, 135℃, 1000Hrs |
Tensile Strength (Thermal Aging) | 93 % | ASTM D573 | Retention, 150℃, 168Hrs |
Elongation (Thermal Aging) | 88 % | ASTM D573 | Retention, 135℃, 1000Hrs |
Elongation (Thermal Aging) | 81 % | ASTM D573 | Retention, 150℃, 168Hrs |
Volume Change | 73 % | ASTM D471 | ASTM Oil#3, 125℃, 70Hrs |
| Industry Category: | Rubber & Plastics/Thermoplastic Elastomers/TPV (Thermoplastic Vulcanizate) |
|---|---|
| Product Category: | |
| Brand: | |
| Spec: | |
| Stock: | |
| Origin: |