Sarlink TPV 4155 - Tubing Extrusion Grade
Price:35
Other Products
Description
Additional Information
Sarlink TPV 4155 - Tubing Extrusion Grade is a globally recognized brand of thermoplastic vulcanizate, an innovative material with rubber-like properties that can be processed like plastic. Sarlink offers time-tested TPV expertise, a wide product range, exceptional customer service, and fully colorable high-performance solutions for many complex application challenges.
Sarlink TPV 4155 - Tubing Extrusion Grade features: The material excels in oil resistance, heat resistance, and rubber-like properties.
| Sarlink TPV 4155 - Tubing Extrusion Grade Product Features | Heat Resistance Oil Resistance | |||
| Sarlink TPV 4155 - Tubing Extrusion Grade Molding Methods | Injection Molding Extrusion | |||
Technical Parameters
| Physical Properties | Value/Unit | Test Standard | Test Conditions |
|---|---|---|---|
Density | 0.97 g/cm3 | ASTM D792 | |
Shrinkage | |||
Longitudinal (Flow) | 2.2 % | Internal | 3mm thickness |
Transverse (Across Flow) | 1.4 % | Internal | 3mm thickness |
| Mechanical Properties | Value/Unit | Test Standard | Test Conditions |
Tensile Strength | |||
At 100% Elongation | 2.1 MPa | ASTM D 412 | Cross direction |
At 100% Elongation | 2.4 MPa | ASTM D 412 | Flow direction |
- | 5.2 MPa | ASTM D 412 | Cross direction |
- | 3.6 MPa | ASTM D 412 | Flow direction |
Elongation at Break | |||
Break (brk) | 427 % | ASTM D 412 | Cross direction |
Break (brk) | 241 % | ASTM D 412 | Flow direction |
Tear Strength | 23 kN/m | ASTM D 624 | Unnicked, Cross direction |
Compression Set | 37 % | ASTM D 395 | 125℃, 70Hrs |
Compression Set | 14 % | ASTM D 395 | 23℃, 22Hrs |
Compression Set | 23 % | ASTM D 395 | 70℃, 22Hrs |
| Impact Properties | Value/Unit | Test Standard | Test Conditions |
Brittleness Temperature | -62 °C | ISO 812 | |
| Hardness Properties | Value/Unit | Test Standard | Test Conditions |
Shore Hardness A | 53 A | ASTM D 2240 | 5sec, Extruded sample |
Shore Hardness A | 56 A | ASTM D 2240 | 5sec, Injection molded sample |
| Flammability Properties | Value/Unit | Test Standard | Test Conditions |
UL Flame Rating | |||
HB | - mm | UL94 | |
| Aging Properties | Value/Unit | Test Standard | Test Conditions |
Hardness (Heat Aging) | 2 - | ASTM D573 | Change, 135℃, 1000Hrs |
Hardness (Heat Aging) | 2 - | ASTM D573 | Change, 150℃, 168Hrs |
Tensile Strength (Heat Aging) | 90 % | ASTM D573 | Retention, 135℃, 1000Hrs |
Tensile Strength (Heat Aging) | 87 % | ASTM D573 | Retention, 150℃, 168Hrs |
Elongation (Heat Aging) | 96 % | ASTM D573 | Retention, 135℃, 1000Hrs |
Elongation (Heat Aging) | 90 % | ASTM D573 | Retention, 150℃, 168Hrs |
Volume Change | 83 % | ASTM D471 | ASTM Oil# |