Sarlink TPV 4190
Price:35
Other Products
Description
Additional Information
Sarlink TPV 4190 Product Characteristics | Heat ResistanceOil Resistance | |||
| Sarlink TPV 4190 Molding Methods | Injection MoldingExtrusion | |||
Sarlink TPV 4190 Technical Parameters
| Physical Properties | Value/Unit | Test Standard | Test Conditions |
|---|---|---|---|
Density | 0.96 g/cm3 | ASTM D792 | |
Shrinkage | |||
Longitudinal (Flow) | 1.7 % | Internal | 3mm thickness |
Transverse (Across Flow) | 1.4 % | Internal | 3mm thickness |
| Mechanical Properties | Value/Unit | Test Standard | Test Conditions |
Tensile Strength | |||
At 100% Elongation | 6.7 Mpa | ASTM D 412 | Cross direction |
At 100% Elongation | 7.7 Mpa | ASTM D 412 | Flow direction |
- | 14.8 Mpa | ASTM D 412 | Cross direction |
- | 13 Mpa | ASTM D 412 | Flow direction |
Elongation at Break | |||
Break (brk) | 577 % | ASTM D 412 | Cross direction |
Break (brk) | 524 % | ASTM D 412 | Flow direction |
Tear Strength | 56 kN/m | ASTM D 624 | Unnicked, Cross direction |
Compression Set | 59 % | ASTM D 395 | 125℃, 70Hrs |
Compression Set | 39 % | ASTM D 395 | 23℃, 22Hrs |
Compression Set | 40 % | ASTM D 395 | 70℃, 22Hrs |
| Impact Properties | Value/Unit | Test Standard | Test Conditions |
Brittleness Temperature | -59 °C | ISO 812 | |
| Hardness Properties | Value/Unit | Test Standard | Test Conditions |
Shore A Hardness | 86 A | ASTM D 2240 | 5sec, Extruded sample |
Shore A Hardness | 88 A | ASTM D 2240 | 5sec, Injection molded sample |
| Flammability Properties | Value/Unit | Test Standard | Test Conditions |
UL Flame Rating | |||
HB | - mm | UL94 | |
| Aging Properties | Value/Unit | Test Standard | Test Conditions |
Hardness (Heat Aging) | 2 - | ASTM D573 | Change, 135℃, 1000Hrs |
Hardness (Heat Aging) | 3 - | ASTM D573 | Change, 150℃, 168Hrs |
Tensile Strength (Heat Aging) | 92 % | ASTM D573 | Retention, 135℃, 1000Hrs |
Tensile Strength (Heat Aging) | 90 % | ASTM D573 | Retention, 150℃, 168Hrs |
Elongation (Heat Aging) | 84 % | ASTM D573 | Retention, 135℃, 1000Hrs |
Elongation (Heat Aging) | 83 % | ASTM D573 | Retention, 150℃, 168Hrs |
Volume Change | 56 % | ASTM D471 |
| Industry Category: | Rubber & Plastics/Thermoplastic Elastomers/TPV (Thermoplastic Vulcanizate) |
|---|---|